Abstract
Aiming at the acid mine drainage (AMD) in zinc, copper and other heavy metals treatment difficulties, severe pollution of soil and water environment and other problems. Through the ultrasonic precipitation method, this study prepared fly ash-loaded nano-FeS composites (nFeS-F). The effects of nFeS-F dosage, pH, stirring rate, reaction time and initial concentration of the solution on the adsorption of Zn(II) and Cu(II) were investigated. The data were fitted by Lagergren first and second-order kinetic equations, Internal diffusion equation, Langmuir and Freundlich isotherm models, and combined with SEM, TEM, FTIR, TGA, and XPS assays to reveal the mechanism of nFeS-F adsorption of Zn(II) and Cu(II). The results demonstrated that: The removal of Zn(II) and Cu(II) by nFeS-F could reach 83.36% and 70.40%, respectively (The dosage was 8 g/L, pH was 4, time was 150 min, and concentration was 100 mg/L). The adsorption process, mainly chemical adsorption, conforms to the Lagergren second-order kinetic equation (R2 = 0.9952 and 0.9932). The adsorption isotherms have a higher fitting degree with the Langmuir model (R2 = 0.9964 and 0.9966), and the adsorption is a monolayer adsorption process. This study can provide a reference for treating heavy metals in acid mine drainage and resource utilization of fly ash.
Similar content being viewed by others
Introduction
The pollution of heavy metals in the water environment has become an important and challenging problem in environmental pollution control1. Among them, the irrational development and utilization of mineral resources have resulted in the generation of substantial volumes of acid mine drainage (AMD) characterized by low pH levels and the presence of various heavy metals such as iron (Fe), manganese (Mn), lead (Pb), copper (Cu), zinc (Zn), among others2. Direct discharge can seriously threaten the soil and water environment and human health3. Currently, the commonly used treatment methods include the adsorption method4,5, biological method6,7, and ion exchange method8,9. Nevertheless, these methods still have some limitations in practical application due to the need for additional adsorbents, carbon sources, and long treatment cycles. However, the chemical precipitation method is often used to treat high-concentration acidic copper and zinc wastewater because of its simple operation, economical and efficient10,11.
Nano-FeS has the advantages of a large specific surface area and strong reducibility, which is considered an efficient reducing agent for treating wastewater containing copper and zinc12. Chen13 investigated the effect of nano-FeS sol on the treatment of simulated electroplating wastewater containing Cu(II) by batch experiments, and the results showed that the treated wastewater can meet the requirements of the national electroplating wastewater discharge standard (GB21900-2008). Tu14 explored the effect of powder and nano-FeS on the remediation of heavy metal-contaminated soil, and the results showed that the effect of nano-FeS on the remediation of Zn-contaminated soil was better than that of powder FeS, the reason is that nano-FeS has a larger specific surface area. Nevertheless, due to the high surface energy of nano-FeS, direct use is easy to cause oxidative agglomeration; it is necessary to seek stable materials as carriers to enhance the stability of nano-FeS15. Sun et al.16 developed Al2O3-supported nano-FeS (FeS/Al2O3), and the results show that FeS/Al2O3 can uniformly disperse FeS and inhibit its agglomeration, increasing the stability of FeS. Wang et al.17 compared the adsorption capacity of chert-coated nano-FeS before and after the adsorption of As(V) by batch adsorption experiments, and the results showed the maximum adsorption of As(V) by the chert after encapsulation of FeS is 30 times higher than that of the chert. The research group has achieved good results by loading nano-FeS onto lignite in the early stage18. However, most of the above carrier materials have the problem of high cost. Therefore, it is necessary to select economically stable carrier materials further.
As a solid waste from coal combustion, fly ash is commonly used in the adsorption treatment of wastewater containing heavy metals because of its large specific surface area and developed pore structure19,20. Mohan et al.21 investigated the adsorption effect of fly ash on Zn(II) and Cu(II) under different conditions by batch experiments, and the results showed that when fly ash concentration is 2 g/L, the removal rates of Zn(II) and Cu(II) were 42% and 39%, respectively. Liu et al.22 prepared tetraethylenepentamine-poly thiocarbamate (TEPAMDT) modified fly ash (MFA), and the results showed that when the concentration of Cu(II) is 100 mg/L, the removal rate of Cu(II) can reach 50% when the concentration of MFA is 412 mg/L. In summary, fly ash as an adsorption material; its unit removal is not high, it has a low adsorption rate, and the conventional modification method has a specific limit on improving its adsorption capacity. Therefore, choosing a reasonable method to treat fly ash is necessary.
Based on this, the present writer prepared fly ash-loaded nano-FeS composites (nFeS-F) through the ultrasonic precipitation method. The nFeS-F not only improves the removal ability of fly ash to Zn(II) and Cu(II) but also solves the problem of easy agglomeration of nano-FeS, provides a surface carrier for nano-FeS, and enhances mechanical strength. Moreover, the effects of nFeS-F dosage, initial pH, stirring rate, reaction time, and initial concentration on Zn(II) adsorption and Cu(II) were investigated. Combined with adsorption kinetics, adsorption isotherms, thermodynamics, SEM, TEM, FTIR, TGA, and XPS, revealed the adsorption mechanism of nFeS-F nFeS-F on Zn(II) and Cu(II). This study can effectively solve the difficult problem of treating heavy metals in acid mine wastewater, and can also broaden the way for the resource utilization of fly ash to achieve the economic and social benefits of treating waste with waste.
Materials and methods
Materials
Fly ash: It was taken from Fuxin City, Liaoning Province, China (42.01°N, 121.65°E). After the screening, it was soaked in deionized water thrice and dried at 105 °C for later use. The main chemical composition is shown in Table 1.
Experimental water samples: Based on measured data of acid mine wastewater from a coal mine in Yulin City, Shaanxi Province, China. The pH of the simulated acidic wastewater containing copper and zinc was set to 4 (The usage of 0.1 mol/L HNO3 and 0.1 mol/L NaOH adjusted), and the appropriate amount of CuSO4·5H2O and ZnSO4·7H2O (the reagents were produced by China Pharmaceutical Group Chemical Reagent Co., Ltd., analytical purity) was dissolved in deionized water to obtain a concentration of 100 mg/L Zn(II) and Cu(II) mixed solution.
Preparation of nFeS-F
Add 4 g fly ash to 200 mL Na2S solution, magnetically stir for 8 h, stand for 5 min, and pour out the Na2S solution. Place the conical flask with fly ash particles in the ultrasonic cleaner, config 200 mL of FeSO4 solution according to a certain iron-sulfur molar ratio, and add FeSO4 solution dropwise to the conical flask at room temperature through a peristaltic pump with a constant flow rate, stir with a mechanical stirrer at 350 rpm, and ultrasonicate at 40 kHz for 10 min. Centrifugation, repeated cleaning with deionized water three times refrigerated sealed spare.
Characterization and detection
The micro-analysis of the nFeS-F and fly ash before and after adsorption by scanning electron microscope (SEM, SIGMA500, Germany). The nFeS-F image was acquired under transmission electron microscopy (TEM, Themis Z, USA). The functional groups of fly ash and nFeS-F before and after adsorption were identified by spectrophotometer (FTIR, Perkinelmer-1000, Germany) in the 400–4000 cm−1 range. The thermogravimetric analysis was done by Netzsch (TGA, STA 449C, Germany). The changes of element and metal valence before and after adsorption were determined by X photoelectron spectrometer (XPS, ESCALAB 250, Britain).
The concentration of Zn(II) and Cu(II) was measured using a Z-2000 flame atomic spectrophotometer (HITACHI), and the pH was measured using the pH-100 pH meter (LICHEN).
Experimental methods
The effect of dosage
At room temperature (298.15 K), nFeS-F with masses of 2 g/L, 4 g/L, 6 g/L, 8 g/L, and 10 g/L were added to 200 mL of Zn(II) and Cu(II) simulated wastewater with an initial concentration of 100 mg/L, respectively (the control groups were all set to add the corresponding grams of fly ash with the particle size of 120–150 mesh to the wastewater). The pH of the simulated water samples was adjusted (pH 4). The samples were taken after stirring at 400 rpm for 150 min. The experiment set up three parallel groups; the mean value was taken as the final value.
The removal rates of Zn(II) and Cu(II) (η, %) and adsorption capacity (qe, mg/g) were calculated using Eqs. (1) and (2).
where: C0 is the initial concentration of the solution, mg/L; Ct is the equilibrium concentration of the solution, mg/L; Ce is the mass concentration of the remaining heavy metal ions in the solution at equilibrium, mg/L; V is the volume of the solution, L; m is the mass of the adsorbent, g.
The effect of initial pH
At room temperature, nFeS-F with a mass of 8 g/L was weighed and added to 200 mL of Zn(II) and Cu(II) simulated wastewater with an initial concentration of 100 mg/L, and the pH of the simulated water samples was adjusted (pH 3, 4, 5, 6, 7), respectively. After stirring at 400 rpm for 150 min, samples were taken and tested. The experiment set up three parallel groups; the mean value was taken as the final value.
The effect of stirring rate
At room temperature, nFeS-F with a mass of 8 g/L was taken and added to 200 mL of simulated wastewater with an initial concentration of 100 mg/L of Zn(II) and Cu(II), respectively, and the pH of the simulated water samples was adjusted (pH 4). Samples were taken at 250 rpm, 300 rpm, 350 rpm, 400 rpm, and 450 rpm after stirring for 150 min. Three groups of parallel experiments were set up, and the mean value was taken as the final value.
The effect of reaction time
At room temperature, nFeS-F with a mass of 8 g/L was added to 200 mL of Zn(II) and Cu(II) simulated wastewater with an initial concentration of 100 mg/L, and the pH of the simulated water samples was adjusted (pH 4), respectively. After stirring at 400 rpm speed for 5 min, 10 min, 20 min, 30 min, 40 min, 50 min, 60 min, 90 min, 120 min, and 150 min, the samples were sampled and detected. The experiment set up three parallel groups; the mean value was taken as the final value.
The effect of initial concentration
At room temperature, nFeS-F with a mass of 8 g/L was weighed and added to 200 mL of simulated wastewater with initial concentrations of 60 mg/L, 100 mg/L, 140 mg/L, 180 mg/L, and 200 mg/L of Zn(II) and Cu(II), respectively, and the pH of the simulated water samples was adjusted (pH 4). After stirring at 400 rpm for 150 min, samples were taken and tested. The experiment set up three parallel groups; the mean value was taken as the final value.
Adsorption kinetics
The solution was prepared with a pH of 4 and an initial concentration of Zn(II) and Cu(II) of 100 mg/L, respectively. The nFeS-F and fly ash with a mass of 8 g/L were added to 200 mL simulated wastewater and stirred at 400 rpm for 5 min, 10 min, 20 min, 30 min, 40 min, 50 min, 60 min, 90 min, 120 min, and 150 min at room temperature. After that, the Zn(II) and Cu(II) concentrations were sampled and detected.
The Zn(II) and Cu(II) adsorption data on nFeS-F and fly ash were linearly fitted by Lagergren first-order kinetic equation, Lagergren second-order kinetic equation, and internal diffusion equation23.
First-order kinetic Eq. (3)24:
Second-order kinetic Eq. (4)25:
where: qt is the adsorption capacity at time t, mg/g; qe is the adsorption capacity at equilibrium, mg/g; K1 is the first-order adsorption rate constant, min; K2 is the second-order adsorption rate constant, mg/(g min); Kp is the internal diffusion rate constant, mg/(g·min1/2); C is a parameter related to the boundary layer, mg/g.
Adsorption isotherms
The pH of the prepared solution was 4 and the initial concentrations of Zn(II) and Cu(II) were 60 mg/L, 100 mg/L, 140 mg/L, 180 mg/L, and 200 mg/L, respectively. Adding nFeS-F and fly ash with a mass of 8 g/L to 200 mL of simulated wastewater, stirred at 400 rpm for 150 min at room temperature, detected the concentration of Zn(II) and Cu(II) after sampling.
The Langmuir isotherm model and Freundlich isotherm model were used to linearly fit the adsorption of fly ash and nFeS-F on Zn(II) and Cu(II)27.
Langmuir isotherm model28 (6):
Freundlich isotherm model29 (7):
where: Ce is the equilibrium concentration, mg/L; qe is the adsorption capacity at equilibrium, mg/g; qm is the saturated adsorption capacity, mg/g; KL is the adsorption constant of Langmuir model; KF is the adsorption constant of Freundlich model; n is the adsorption strength correlation constant.
Adsorption thermodynamics
To better understand the thermodynamic characteristics of the reaction process, the primary forces governing the adsorption were elucidated by computing the thermodynamic constants for the adsorption of nFeS-F onto Zn(II) and Cu(II). The relevant thermodynamic equations are shown in (8)–(10).
where: Kc represents the solid–liquid partition coefficient (L/g); R denotes the ideal gas constant, 8.314 × 10−3 kJ/(mol K); T signifies the absolute temperature in thermodynamics (K); qe denotes the equilibrium adsorption amount (mg/g); Ce stands for the equilibrium concentration (mg/L); ΔG indicates the standard Gibbs free energy (kJ/mol); ΔH represents the standard enthalpy change of adsorption (kJ/mol); ΔS denotes the standard entropy change of adsorption kJ/(mol K).
The effect of coexisting ions and ionic strength
In natural aquatic environments, the presence of Zn(II) and Cu(II) often coincides with other heavy metal ions, potentially influencing their removal by nFeS-F. This investigation delved into the impact of coexisting ions and ionic strength on the removal of Zn(II) and Cu(II), utilizing Cd(II) and Ni(II) as representative species.
Leaching toxicity of nFeS-F
The leaching toxicity of fly ash and nFeS-F was investigated to assess the safety of these materials in water treatment applications. Heavy metal content in the leachate was determined using a flame atomic spectrophotometer, following the guidelines outlined in the Chinese national standards GB 5085.3–2007 and HJ/T 299–200730.
Results and discussion
Characterizations
SEM analysis
Figure 1 displays the SEM image of the surface morphology of fly ash and nFeS-F before and after adsorption. As shown in Fig. 1a, fly ash is mainly composed of smooth glassy spheres, irregularly surfaced porous particles, and a small amount of unburned carbon31. By comparing Fig. 1a and b, it can be seen that the vitreous structure of fly ash was destroyed after adsorption, the surface roughness increased significantly, and many fine sediments were attached. The sediment crystals may be hydroxide precipitates of Cu(II) and Zn(II). It can be seen from Fig. 1c and d that many flake crystals appear on the surface of fly ash, indicating that nano-FeS is uniformly loaded onto fly ash and the carrier structure is complete. However, after adsorption, the nano-FeS crystals decreased, and the surface of the carrier became rough. At the same time, particle deposition appeared on the surface and pores of nFeS-F particles. The particles should be CuS and ZnS precipitates formed by the reaction of nano-FeS with Cu(II) and Zn(II)32.
TEM analysis
As depicted in Fig. 1e and f, the FeS crystals exhibit a flaky morphology and are uniformly dispersed across the surface of the fly ash, with an average length ranging from 40 to 80 nm. This morphology bears a resemblance to the nano FeS synthesized by Wang et al.33, thereby suggesting, in conjunction with SEM analysis, the efficacy of the ultrasonic precipitation method in loading nano FeS onto fly ash particles. The uniform distribution of nanocrystals on nFeS-F signifies that using fly ash as a carrier can notably enhance the dispersion and stability of nano-FeS, regulate particle size, and effectively mitigate nanoparticle agglomeration.
FTIR analysis
The FTIR spectra of fly ash before and after adsorption of nFeS-F are shown in Fig. 2a. It can be seen that nFeS-F appears to have a solid and broad absorption peak near 3346 cm−1, corresponding to the stretching vibration peak of –OH, indicating that there is a certain amount of hydroxyl group on the surface of nFeS-F34. At 1653.89 cm-1, H–O–H bending vibration may be the dissipation of bound water on the surface of fly ash. By reducing the adsorption resistance of water film to pollutants, the adsorption of Zn(II) and Cu(II) is enhanced35. 1066 cm−1, 778 cm−1, and 457 cm–1 correspond to the asymmetric tensile vibration peak of silica tetrahedron of fly ash, the symmetric stretching vibration peak of Si–O–Si and the bending vibration peak of Si–O, respectively36. In previous reports, FeS did not have a prominent absorption peak. In the spectrum of nFeS-F, the bending vibration peak of Si–O moved to the right to 415 cm−1, and the intensity of the peak decreased, which may be due to the adhesion of FeS on the surface of fly ash. At the same time, a microstrip of Fe–O groups appeared at 612 cm−1, indicating that FeS was oxidized and attached to the surface of nFeS-F through functional groups such as –OH and –C=O37. The tensile peak strength of –OH was observed to decrease in the nFeS-F adsorption spectrum, indicating that the hydroxyl group played a certain role in the removal of Zn(II) and Cu(II)38.
TGA analysis
Thermogravimetric analysis was used to explain the thermal stability and weight loss behavior of fly ash and nFeS-F under a nitrogen atmosphere from 50 °C up to 800 °C. The results of the analysis are shown in Fig. 2b. It was observed that the TGA curve of the fly ash did not change significantly in the tested temperature range, and the total weight loss was only 1.2%, which may be due to the loss of small amount of unburned carbon and moisture in the fly ash, indicating that the fly ash is thermally stable39. In contrast, there are two main stages in the weight change mitigation of the thermal decomposition of nFeS-F. Initially, the water on the surface of the material starts to disappear at 110 °C due to the evaporation of the water adsorbed on the surface of nFeS-F, which involves Vander walls force of attraction within molecules40. The second weight loss occurred between 200 °C and 480 °C, indicating that FeS underwent oxidative pyrolysis and dissipated as the gaseous products SO2 and SO341.
XPS analysis
The changes in elements and valence states before and after the interaction between Zn(II), Cu(II), and nFeS-F were further discussed by XPS analysis. By comparing the changes in the whole spectrum and the relative atomic content before and after the adsorption of Zn(II) and Cu(II) by nFeS-F (Fig. 3, Table 2), the relative atomic content of Fe 2p decreased from 3.91% to 2.44%, and the relative atomic content of S 2p decreased from 3.31% to 2.23% after nFeS-F treatment of wastewater, indicating that FeS participated in the chemical reaction. At the same time, Zn 2p and Cu 2p appeared in the adsorbed nFeS-F, and the relative atomic contents were 1.73% and 2.92%, respectively, indicating that nFeS-F had a particular ability to fix zinc and copper. It can be seen that the peak separation diagram of Zn 2p corresponds to the characteristic peak of ZnS at 1021.8 eV. The peak of Cu 2p corresponds to the characteristic peak of CuS at 932.1 eV35, indicating that Cu(II) and Zn(II) were successfully immobilized on the surface of nFeS-F.
The effect of dosage
It can be seen from Fig. 4a and b that the removal rates of Zn(II) and Cu(II) increased with the increase of nFeS-F dosage. When the dosage is 2.0 g/L ~ 8.0 g/L, compared with the original fly ash, nFeS-F has apparent advantages, and the removal rate of Zn(II) and Cu(II) increased rapidly, and it increased from 49.50% to 79.92% and from 21.19% to 68.54%, respectively. When the dosage was more than 8.0 g/L, the removal rate of Zn(II) and Cu(II) did not increase significantly, indicating that the adsorption reached saturation when the dosage of nFeS-F was 8.0 g/L, which was the best dosage. Before reaching equilibrium, increasing the dosage of nFeS-F can provide more adsorption sites for Zn(II) and Cu(II) and rapidly increase the removal rate42. After reaching equilibrium, the removal effect of nFeS-F is not apparent. The reason is that the concentration of Zn(II) and Cu(II) has been determined, and it is difficult to improve the removal rate even if the dosage of nFeS-F is increased43. Therefore, the dosage of nFeS-F in subsequent experiments was set to 8.0 g/L.
The effect of initial pH
It can be seen from Fig. 4c and d that the removal rates of Zn(II) and Cu(II) decreased gradually with the increase of solution pH. When the pH was 3 ~ 7, the removal rates decreased from 79.21% to 44.36% and from 69.32% to 42.31%, respectively. The reason is that under weak acid conditions, FeS has better solubility and can release more Fe(II) to rapidly reduce Cu(II) and Zn(II)44. In addition, Cu(II) and Zn(II) have a smaller solubility product, which makes it easier to react with S(–II) in the solution to form insoluble precipitates such as CuS and ZnS. As the pH continues to increase, the solubility of FeS gradually decreases, and the precipitation of insoluble substances decreases, resulting in a decrease in the removal rate. Considering the situation comprehensively, the pH was set to 4.
The effect of stirring rate
From Fig. 4e and f, it is evident that the removal efficiencies of both Zn(II) and Cu(II) exhibit an initial increase followed by reaching equilibrium as the stirring rate is intensified. Removing Zn(II) and Cu(II) by nFeS-F demonstrated an escalation from 65.89% to 82.57% and 52.64% to 70.14%, respectively, as the rotational speed elevated from 250 rpm to 450 rpm. This observation suggests that the interaction between nFeS-F and metal molecules is insufficient at lower stirring rates, constraining the solid–liquid phase mass transfer of Zn(II) and Cu(II) on nFeS-F45. Stirring rates surpassing 400 rpm yielded marginal increments in Zn(II) and Cu(II) removal efficiencies, indicative of the reaction gradually approaching equilibrium. Consequently, considering all factors, a stirring rate of 400 rpm was chosen for subsequent experiments.
The effect of reaction time
It can be seen in Fig. 5a and b that with the increase of reaction time, the removal rates of Zn(II) and Cu(II) by nFeS-F increased rapidly from 39.45% to 70.51% and 40.21% to 63.47%, respectively. Then, the growth rate gradually decreased (Fig. 3). When carried out the reaction of nFeS-F to Zn(II) and Cu(II) for 90 min and 150 min, the removal rates of Zn(II) and Cu(II) were relatively weak, indicating that the reaction had reached equilibrium. The loaded fly ash can provide more adsorption sites for Zn(II) and Cu(II). At the same time, acidic conditions will promote the rapid dissolution of FeS so that Zn(II) and Cu(II) react with S(–II) to form insoluble sulfides and are removed. When the adsorption time is 0–60 min, Zn(II) and Cu(II) will preferentially enter the surface micropores of nFeS-F. At this time, the concentration of Zn(II) and Cu(II) in the solution is higher, and the adsorption reaction potential kinetic energy is higher, so the removal rate is faster. After the adsorption time continues to increase, the relative content of active sites of nFeS-F gradually decreases, and the mass transfer rate decreases. Considering the situation comprehensively, the reaction time was set at 150 min.
The effect of initial concentration
It can be seen from Fig. 5c and d that the removal rate of Zn(II) and Cu(II) by nFeS-F is higher when the initial concentration of the solution is low. With the increase of the initial concentration of the solution, the increase of the unit adsorption capacity of nFeS-F to Zn(II) and Cu(II) gradually slowed down, and the removal rate of Zn(II) decreased from 92.69% to 41.54%, when the initial concentration was 60 mg/L to 100 mg/L, the unit adsorption capacity increased from 6.95 mg/g to 10.08 mg/g. When the initial concentration was 100 mg/L to 200 mg/L, the unit adsorption capacity increased slowly. The removal rate of Cu(II) decreased from 78.23% to 34.60%. When the initial concentration was 60 mg/L to 100 mg/L, the unit adsorption capacity increased from 5.87 mg/g to 8.76 mg/g. When the initial concentration was 100 mg/L to 200 mg/L, the unit adsorption capacity increased slowly. Because the initial concentration of Zn(II) and Cu(II) increased, the supply of adsorption sites on the surface of the adsorbent was insufficient, resulting in a decrease in the removal rate. The partial sulfide precipitation formed by the reaction of S(–II) with Zn(II) and Cu(II) blocked the pores of the adsorbent and gradually reached equilibrium46. Therefore, the initial concentration of Zn(II) and Cu(II) in the subsequent test was set at 100 mg/L.
Adsorption kinetic analysis
The fitting curves and parameters of Zn(II) and Cu(II) are obtained by kinetic equations. The results are shown in Fig. 6 and Table 3.
It can be seen from Table 3 that the correlation coefficient R2 of the second-order kinetic equation is higher than that of the first-order kinetic equation, which is 0.9952 and 0.9932, respectively. The calculated theoretical saturated adsorption capacity (qe = 10.7458 mg/g, 9.1249 mg/g) is close to the experimental adsorption capacity (qm = 10.42 mg/g, 8.80 mg/g), indicating that the adsorption of Zn(II) and Cu(II) by nFeS-F conforms to the second-order kinetic equation: t/qt = 0.09306t + 0.9999; t/qt = 0.10959t + 1.0000, adsorption is mainly chemical adsorption process47. It can be seen that the internal diffusion equation curve is a continuous multi-segment curve (Fig. 6), indicating that the adsorption of Zn(II) and Cu(II) by nFeS-F is affected by both membrane diffusion and internal diffusion48. Zn(II) and Cu(II) adsorption from the liquid phase to nFeS-F includes three stages49. The first stage is mainly the initial stage of adsorption. Zn(II) and Cu(II) in the solution diffuse to the surface of nFeS-F and occupy the adsorption sites on the surface of nFeS-F. The second stage is internal diffusion. Zn(II) and Cu(II) enter the pores and are adsorbed after reaching the surface of nFeS-F. The third stage is the adsorption equilibrium stage, and the adsorption gradually reaches saturation.
Adsorption isotherm analysis
The adsorption isotherm models were used to fit the experimental data. The obtained adsorption isotherm results are shown in Fig. 7. The fitting equation and specific parameters are shown in Table 4.
It can be seen in Fig. 7 and Table 4 that the Langmuir fitting curve equations of fly ash and nFeS-F to Cu(II) are as follows: ce/qe = 5.35332ce + 0.1528, R2 = 0.9646, qm = 0.1868 mg/g; ce/qe = 0.38613ce + 0.1114, R2 = 0.9966, qm = 2.5898 mg/g. The Freundlich fitting curve equations are lnqe = 0.41322lnce-0.4367, R2 = 0.9119; lnqe = 0.22472lnce + 1.1295, R2 = 0.9475; The Langmuir fitting curve equations of fly ash and nFeS-F to Zn(II) are ce/qe = 0.08571ce + 0.1790, R2 = 0.9964, qm = 11.6670 mg/g; ce/qe = 0.15444ce + 0.0947, R2 = 0.9998, qm = 6.4751 mg/g. The Freundlich fitting curve equations are lnqe = 0.14164lnce + 0.9974, R2 = 0.9600; lnqe = 0.13158lnce + 1.7431, R2 = 0.9268. Comparing the correlation coefficient R2, it can be seen that the Langmuir isotherm fitting of Cu(II) and Zn(II) adsorbed by fly ash and nFeS-F is higher, so the adsorption process is dominated by monolayer adsorption. The adsorption strength n of the Freundlich model is greater than 1, indicating that the adsorption process is easy to carry out50. The KF of fly ash and nFeS-F were 0.6462, 2.7113, and 3.0943, 5.7153, respectively. The size of KF was proportional to the adsorption capacity and adsorption strength. By comparison, nFeS-F can effectively improve wastewater-containing Cu(II) and Zn(II) treatment.
Adsorption thermodynamic analysis
Figure 8 presents the Van't Hoff plots of lnKc against 1/T to determine ∆H and ∆S values. When coupled with Table 5, it becomes evident that the ∆G values for Zn(II) and Cu(II) are consistently negative across all temperatures, diminishing as temperature rises. Conversely, ∆H exhibits a positive trend, suggesting that the adsorption process of nFeS-F onto Zn(II) and Cu(II) is a spontaneous heat-absorption reaction. Furthermore, the temperature elevation proves advantageous for the adsorption of nFeS-F onto Zn(II) and Cu(II)51. Positive ΔS values indicate an augmentation in the randomness of the nFeS-F surface, while smaller ΔS values denote a subtle alteration in the adsorbent structure52. Table 6 presents a comparative analysis between nFeS-F and other documented adsorbents. When juxtaposed with the adsorbents reported in the literature, nFeS-F exhibits superior Zn(II) and Cu(II) adsorption capacities.
The effect of coexisting ions and ionic strength
The analysis of Fig. 9 reveals that coexisting cations hindered the removal efficiency of Zn(II) and Cu(II), with the inhibition effect correlating with the ionic strength. This phenomenon arises from the competitive interaction of coexisting cations with Zn(II) and Cu(II) for adsorption sites, diminishing the electrostatic attraction between nFeS-F and the target ions and reducing removal efficiency. Elevated ionic strength fosters the agglomeration of FeS nanoparticles, thereby diminishing specific surface area and amplifying their inhibitory impact59. Furthermore, the competitive adsorption of Ni(II) on Zn(II) and Cu(II) systems surpassed that of Cd(II), likely due to the smaller ionic radius and higher electronegativity of Ni(II)60. Consequently, the influence exerted by Cd(II) and Ni(II) on the adsorption of Zn(II) and Cu(II) by nFeS-F ranks as Ni(II) > Cd(II).
Leaching toxicity of nFeS-F
Table 7 presents the concentrations of main heavy metals in the leach solution of both fly ash and nFeS-F, encompassing total chromium, lead (Pb), copper (Cu), cadmium (Cd), zinc (Zn), and nickel (Ni). Certain heavy metal levels in the fly ash leachate surpassed corresponding regulatory thresholds. Conversely, concentrations of primary heavy metals in the nFeS-F leachate remained below the limits stipulated for direct discharge of water pollutants (as per GB25467-201061) and the standard values for assessing leaching toxicity (GB 5085.3-200762). Suggests that nFeS-F exhibits a commendable ability to immobilize heavy metal ions. Furthermore, the lower concentrations of primary heavy metals in the nFeS-F leach solution than fly ash imply its reduced potential for causing secondary pollution in water treatment scenarios. Thus, nFeS-F is a promising adsorbent for effectively treating wastewater containing Zn(II) and Cu(II).
Conclusion
This study synthesized fly ash-loaded nano-FeS composites using the ultrasonic precipitation method based on mineral loading technology. This approach addressed the challenges of the low individual adsorption capacity of fly ash and the susceptibility of nano FeS to oxidative agglomeration, thereby enhancing the stability of the composites. The removal efficiency of nFeS-F for Zn(II) and Cu(II) was investigated through static experiments. Results indicated significantly higher removal efficiency of nFeS-F for Zn(II) and Cu(II) in wastewater than fly ash under acidic conditions, achieving up to 83.36% and 70.40%, respectively. Kinetic and isotherm studies revealed that the adsorption process of Zn(II) and Cu(II) by nFeS-F follows a monomolecular layer adsorption mechanism dominated by chemisorption. Thermodynamic analyses demonstrated that the adsorption of Zn(II) and Cu(II) by nFeS-F is spontaneous. Furthermore, leaching experiments illustrated that nFeS-F significantly mitigated the risk of heavy metal leaching, thus positioning it as an efficient and safe adsorbent for practical applications.
Data availability
The datasets used and/or analysed during the current study available from the corresponding author on reasonable request.
References
Shetaia, S. A., Khatita, A. M. A., Abdelhafez, N. A., Shaker, I. M. & Kafrawy, S. B. E. Human-induced sediment degradation of Burullus lagoon, Nile Delta, Egypt: Heavy metals pollution status and potential ecological risk. Mar. Pollut. Bull. 178, 113566 (2022).
Ahmed, R. S., Abuarab, M. E., Ibrahim, M. M., Baioumy, M. & Mokhtar, A. Assessment of environmental and toxicity impacts and potential health hazards of heavy metals pollution of agricultural drainage adjacent to industrial zones in Egypt. Chemosphere 318, 137872 (2023).
Yousaf, A., Athar, M., Salman, M., Farooq, U. & Chawla, F. S. Heavy metal pollution in surface sediments and human health assessment in southern Al-Khobar coast, Saudi Arabia. Mar. Pollut. Bull. 187, 114508 (2023).
Duan, G., Cao, Z., Zhong, H., Ma, X. & Wang, S. Highly efficient poly(6-acryloylamino-N-hydroxyhexanamide) resin for adsorption of heavy metal ions. J. Environ. Manage. 308, 114631 (2022).
FernandezPerez, B., AyalaEspina, J. & FernandezGonzalez, M. L. A. Adsorption of heavy metals ions from mining metallurgical tailings leachate using a shell-based adsorbent: Characterization kinetics and isotherm studies. Materials 15, 5315 (2022).
Peng, Z. et al. Biological treatment of wastewater with high concentrations of zinc and sulfate ions from zinc pyrithione synthesis. Trans. Nonferrous Metals Soc. China 27, 2481–2491 (2017).
Xie, X. et al. Exploration of biomineralization treatment technology for heavy metal pollution. J. Huazhong Univ. Sci. Tech. Nat. Sci. Ed. 51, 122–127 (2023).
Lahiri, S. K., Zhang, C., Sillanpaa, M. & Liu, L. Nanoporous NiO@SiO2 photo-catalyst prepared by ion-exchange method for fast elimination of reactive dyes from wastewater. Mater. Today Chem. 23, 100677 (2022).
Pinelli, D. et al. Ammonium recovery from municipal wastewater by ion exchange: Development and application of a procedure for sorbent selection. J. Environ. Chem. Eng. 10, 108829 (2022).
Che, J., Zhang, W., Ma, B. & Wang, C. An efficient process for recovering copper as CuO nanoparticles from acidic waste etchant via chemical precipitation and thermal decomposition: Turning waste into value-added product. J. Clean. Prod. 369, 133404 (2022).
Xu, R. et al. Removal of heavy metal(loid)s from aqueous solution by biogenic FeS–kaolin composite: Behaviors and mechanisms. Chemosphere 299, 134382 (2022).
Saravanan, A. et al. A review on synthesis methods and recent applications of nanomaterial in wastewater treatment: Challenges and future perspectives. Chemosphere 307, 135713 (2022).
Chen, Y. Study on the treatment of electroplating wastewater with nanoparticle of FeS sol. Ind. Water Treatm. 32, 68–71 (2012).
Tu, M. Study on Remediation of Heavy Metal Contaminated Soil Using Iron Sulfide Nanoparticles (Beijing University of Civil Engineering and Architecture, 2012).
He, M. et al. Reduction characteristics and mechanism of Cr(VI) in water using ascorbic acid modified nanoFeS. Acta Sci. Circum. 43, 61–72 (2023).
Sun, Y. et al. Immobilization of mercury (II) from aqueous solution using Al2O3-supported nanoscale FeS. Chem. Eng. J. 323, 483–491 (2017).
Wang, Y. et al. Research on bio-nano FeS strengthening the capability of limestone for removing arsenic in acid mine drainage. Acta Pet Rol. Mine Ral. 35, 893–900 (2016).
Guo, X. et al. Study on preparation of adsorption material (nano FeS loaded on lignite) and its chromium removal performance. Coal Sci. Technol. 48, 152–159 (2020).
Usman, M., Katsoyiannis, I., Rodrigues, J. H. & Ernst, M. Fly ash adsorbents for multi-cation wastewater treatment. Appl. Surf. Sci. 258, 6345–6352 (2012).
Deng, X., Qi, L. & Zhang, Y. Experimental study on adsorption of hexavalent chromium with microwave-assisted alkali modified fly ash. Water Air Soil Pollut. 229, 18 (2018).
Mohan, S. & Gandhimathi, R. Removal of heavy metal ions from municipal solid waste leachate using coal fly ash as an adsorbent. J. Hazard. Mater. 169, 351–359 (2009).
Liu, L. H., Li, B., Cao, J. & Zhou, Z. H. Modification of fly ash by sodium tetraethylenepentamine-multi dithiocarbamate and its removing performance towards Cu(II). Adv. Mater. Res. 421, 71–76 (2012).
Yu, L. et al. Adsorption behaviors of Pb2+ in wastewater by NaOH modified fly ash. Non-Metal. Mines 44, 80–83 (2021).
Lagergren, S. Y. Zur theorie der sogenannten adsorption geloster stoffe. Veternskapsakad. Handl 24, 1–39 (1898).
Ho, Y. Review of second-order models for adsorption systems. J. Hazard. Mater. 136, 681–689 (2006).
Weber, W. J. & Morris, J. C. Closure to kinetics of adsorption on carbon from solution. J. Sanit. Engrg. Div. 89, 53–55 (1963).
Fu, S. et al. Preparation of lignite-loaded nano-FeS and its performance for treating acid Cr(VI)-containing wastewater. Environ. Sci. Pollut. Res. 30, 3351–3366 (2023).
Langmuir, I. The constitution and fundamental properties of solids and liquids. J. Am. Chem. Soc. 38, 2221–2295 (1916).
Freundlich, H. Uber die adsorption in losungen. Z. Phys. Chem. 57U, 385–470 (1907).
State environmental protection administration of China. Industry Standard of HJ/T 299-2007, Solid Waste Leaching Toxicity Leaching Method Nitric Acid Sulfate Method (China Environmental Science Press, 2007).
Xu, R., Lyu, T. & Wang, L. Utilization of coal fly ash waste for effective recapture of phosphorus from waters. Chemosphere 287, 132431 (2022).
Zhou, J. et al. Utilization of cationic polymer-modified fly ash for dye wastewater treatment. Clean Technol. Environ. Policy 23, 1273–1282 (2021).
Wang, Y. et al. Biochar-supported FeS/Fe3O4 composite for catalyzed fenton-type degradation of ciprofloxacin. Catalysts 9, 1062 (2019).
Liu, R., Zhang, Y., Hu, B. & Wang, H. Improved Pb(II) removal in aqueous solution by sulfide@biochar and polysaccharose-FeS@biochar composites: Efficiencies and mechanisms. Chemosphere 287, 132087 (2022).
Zhao, X. et al. Effect and mechanisms of synthesis conditions on the cadmium adsorption capacity of modified fly ash. Ecotoxicol. Environ. Saf. 223, 112550 (2021).
Wang, L. et al. Stabilization of lead in waste water and farmland soil using modified coal fly ash. J. Clean. Prod. 314, 127957 (2021).
Yang, Y. et al. Adsorption and reduction of Cr(VI) by a novel nanoscale FeS/chitosan/biochar composite from aqueous solution. J. Environ. Chem. Eng. 9, 105407 (2021).
Pant, B. D. et al. Efficient biosorption of hexavalent chromium from water by modified arecanut leaf sheath. Heliyon 8, e09283 (2022).
Van Der Merwe, E. M., Mathebula, C. L. & Prinsloo, L. C. Characterization of the surface and physical properties of South African coal fly ash modified by sodium lauryl sulphate (SLS) for applications in PVC composites. Powder Technol. 266, 70–78 (2014).
Tripathy, S., Sahu, S., Patel, R. K., Panda, R. B. & Kar, P. K. Efficient removal of Cr(VI) by polyaniline modified biochar from date (Phoenix dactylifera) seed. Groundw. Sustain. Dev. 15, 100653 (2021).
Yang, M. et al. Synthesis of carbon nanotubes/FeS fenton-like catalyst and its catalytic properties. Chem. J. Chin. Univ. 35, 570–575 (2014).
Trinh, V. T. et al. Phosphate adsorption by silver nanoparticles-loaded activated carbon derived from tea residue. Sci. Rep. 10, 3634 (2020).
Song, M. Preparation of Lignite-Based Adsorbent and its Adsorption of Cd2+ and Zn2+ in Water and Removal of Dissolved Humic Acid Were Studied (Kunming University of Science and Technology, 2020).
Li, D. et al. Interaction of aqueous antimony(III) with synthetic ferrous sulfide. Appl. Geochem. 128, 104957 (2021).
Sasan Narkesabad, Z., Rafiee, R. & Jalilnejad, E. Experimental study on evaluation and optimization of heavy metals adsorption on a novel amidoximated silane functionalized Luffa cylindrica. Sci. Rep. 13, 3670 (2023).
Adenuga, A. A., Amos, O. D., Oyekunle, J. A. O. & Umukoro, E. H. Adsorption performance and mechanism of a low-cost biosorbent from spent seedcake of Calophyllum inophyllum in simultaneous cleanup of potentially toxic metals from industrial wastewater. J. Environ. Chem. Eng. 7, 103317 (2019).
Bai, S. et al. Removal of heavy metals from aqueous solutions by X-type zeolite prepared from combination of oil shale ash and coal fly ash. Energy Sources A 44, 5113–5123 (2022).
Jiang, C., Wang, R., Chen, X., Zheng, L. & Cheng, H. Preparation of chitosan modified fly ash under acid condition and its adsorption mechanism for Cr(VI) in water. J. Cent. South Univ. 28, 1652–1664 (2021).
Huang, L., Cao, C., Xu, D., Guo, Q. & Tan, F. Intrinsic adsorption properties of raw coal fly ash for quinoline from aqueous solution: kinetic and equilibrium studies. SN Appl. Sci. 1, 1090 (2019).
Mohapatra, R. K., Parhi, P. K. & Pandey, S. Active and passive biosorption of Pb(II)using live and dead biomass of marine bacterium Bacillus xiamenensis PbRPSD202: Kinetics and isotherm studies. J. Environ. Manag. 247, 121–134 (2019).
Rai, R. et al. Acid-treated pomegranate peel: An efficient biosorbent for the excision of hexavalent chromium from wastewater. Heliyon 9, e15698 (2023).
Poudel, B. R. et al. Effective remediation of arsenate from contaminated water by zirconium modified pomegranate peel as an anion exchanger. J. Environ. Chem. Eng. 9, 106552 (2021).
Song, J. et al. Mg Fe-layered double hydroxides (LDHs) modified electrode enhanced capacitive deionization for simultaneous phosphorus recovery and copper ions removal. J. Environ. Chem. Eng. 12, 112145 (2024).
Shi, L.-N., Zhou, Y., Chen, Z., Megharaj, M. & Naidu, R. Simultaneous adsorption and degradation of Zn2+ and Cu2+ from wastewaters using nanoscale zero-valent iron impregnated with clays. Environ. Sci. Pollut. Res. 20, 3639–3648 (2013).
Wang, X. et al. Adsorption of Copper(II) onto activated carbons from sewage sludge by microwave-induced phosphoric acid and zinc chloride activation. Desalination 278, 231–237 (2011).
Wang, C., Wang, J., Wang, S., Yang, R. & Wang, H. Preparation of Mg(OH)2/calcined fly ash nanocomposite for removal of heavy metals from aqueous acidic solutions. Materials 13, 4621 (2020).
Esmaeili, A. & Eslami, H. Adsorption of Pb(II) and Zn(II) ions from aqueous solutions by Red Earth. MethodsX 7, 100804 (2020).
Chaudhry, S. A., Khan, T. A. & Ali, I. Adsorptive removal of Pb(II) and Zn(II) from water onto manganese oxide-coated sand: Isotherm, thermodynamic and kinetic studies. Egypt. J. Basic Appl. Sci. 3, 287–300 (2016).
Zou, H. et al. Ball milling biochar iron oxide composites for the removal of chromium (Cr(VI)) from water: Performance and mechanisms. J. Hazard. Mater. 413, 125252 (2021).
Zhang, M. et al. High and fast adsorption of Cd(II) and Pb(II) ions from aqueous solutions by a waste biomass based hydrogel. Sci. Rep. 10, 3285 (2020).
Ministry of environmental protection and state general administration of quality supervision, inspection and quarantine of China. National Standard of GB 25467-2010, Emission Standards for Industrial Pollutants of Copper, Nickel and Cobalt. (China Environmental Science Press, 2010).
State environmental protection administration of China. National Standard of GB5085.3-2007, Identification Standards for Hazardous Wastes-Identification for Extraction Toxicity. (China Environmental Science Press, 2007).
Acknowledgements
The project is funded by the National Natural Science Foundation of China (51304114, 52304188), Department of Education of Liaoning Province (LJKFZ20220199), Science and Technology Department of Liaoning Province (2023-BS-201), "Double First-class" Innovation Team of Liaoning Technical University (LNTU20TD-21).
Author information
Authors and Affiliations
Contributions
X.G. and Z.H.: Conceptualization; X.G.: methodology; X.G. and H.F.: software; X.G.: validation; X.G.: formal analysis; X.G. and Z.H.: investigation; H.F. and X.G.3: resources; X.G. and H.F.: data curation; H.F.: writing—original draft preparation; Z.H.: writing—review and editing; X.G.: visualization; Z.Z.: supervision; X.G.3 and Z.Z.: project administration; all authors have read and agreed to the published version of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Guo, X., Fu, H., Gao, X. et al. Study on the adsorption of Zn(II) and Cu(II) in acid mine drainage by fly ash loaded nano-FeS. Sci Rep 14, 9927 (2024). https://doi.org/10.1038/s41598-024-58815-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-024-58815-z
Keywords
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.